Polymerization of olefins

ABSTRACT

Mixtures of different polyolefins may be made by direct, preferably simultaneous, polymerization of one or more polymerizable olefins using two or more transition metal containing active polymerization catalyst systems, at least one of which contains cobalt or iron complexed with selected ligands. The polyolefin products may have polymers that vary in molecular weight, molecular weight distribution, crystallinity, or other factors, and are useful as molding resins and for films.

FIELD OF THE INVENTION

Polymers with varied and useful properties may be produced in processesusing at least two polymerization catalysts, at least one of which is aselected iron or cobalt catalyst, for the synthesis of polyolefins.

TECHNICAL BACKGROUND

Polyolefins are most often prepared by polymerization processes in whicha transition metal containing catalyst system is used. Depending on theprocess conditions used and the catalyst system chosen, polymers, eventhose made from the same monomer(s) may have varying properties. Some ofthe properties which may change are molecular weight and molecularweight distribution, crystallinity, melting point, branching, and glasstransition temperature. Except for molecular weight and molecular weightdistribution, branching can affect all the other properties mentioned.

It is known that certain transition metal containing polymerizationcatalysts containing iron or cobalt, are especially useful inpolymerizing ethylene and propylene, see for instance U.S. patentapplication Ser. No. 08/991,372, filed Dec. 16, 1997, and Ser. No.09/006,031, filed Jan. 12, 1998 (“equivalents” of World PatentApplications 98/27124 and 98/30612). It is also known that blends ofdistinct polymers, that vary for instance in molecular weight, molecularweight distribution, crystallinity, and/or branching, may haveadvantageous properties compared to “single” polymers. For instance itis known that polymers with broad or bimodal molecular weightdistributions may often be melt processed (be shaped) more easily thannarrower molecular weight distribution polymers. Also, thermoplasticssuch as crystalline polymers may often be toughened by blending withelastomeric polymers.

Therefore, methods of producing polymers which inherently producepolymer blends are useful especially if a later separate (and expensive)polymer mixing step can be avoided. However in such polymerizations oneshould be aware that two different catalysts may interfere with oneanother, or interact in such a way as to give a single polymer.

Various reports of “simultaneous” oligomerization and polymerization ofethylene to form (in most cases) branched polyethylenes have appeared inthe literature, see for instance World Patent Application 90/15085, U.S.Pat. Nos. 5,753,785, 5,856,610, 5,686,542, 5,137,994, and 5,071,927, C.Denger, et al,. Makromol. Chem. Rapid Commun., vol. 12, p. 697-701(1991), and E. A. Benham, et al., Polymer Engineering and Science, vol.28, p. 1469-1472 (1988). None of these references specifically describesany of the processes herein or any of the branched homopolyethylenesclaimed herein.

SUMMARY OF THE INVENTION

This invention concerns a process for the polymerization of olefins,comprising, contacting under polymerizing conditions:

(a) a first active polymerization catalyst for said olefins which is aFe or Co complex of a ligand of the formula:

wherein:

-   -   R¹, R² and R³ are each independently hydrogen, hydrocarbyl,        substituted hydrocarbyl, or an inert functional group;    -   R⁴ and R⁵ are each independently hydrogen, hydrocarbyl, an inert        functional group or substituted hydrocarbyl; and    -   R⁶ and R⁷ are aryl or substituted aryl;

(b) a second active polymerization catalyst for said olefins whichcontains one or more transition metals;

(c) a least one first olefin capable of being polymerized by said firstactive polymerization catalyst; and

(d) at least one second olefin capable of being polymerized by saidsecond active polymerization catalyst.

This invention also concerns a process for the polymerization ofolefins, comprising, contacting under polymerizing conditions:

(a) a first active polymerization catalyst for said olefins which is aFe or Co complex of a ligand of the formula:

wherein:

-   -   R¹, R² and R³ are each independently hydrogen, hydrocarbyl,        substituted hydrocarbyl, or an inert functional group;    -   R⁴ and R⁵ are each independently hydrogen, hydrocarbyl, an inert        functional group or substituted hydrocarbyl; and    -   R⁶ and R⁷ are aryl or substituted aryl;

(b) a second active polymerization catalyst for said olefins whichcontains one or more transition metals;

(c) a least one first olefin capable of being polymerized by said firstactive polymerization catalyst; and

(d) at least one second olefin capable of being polymerized by saidsecond active polymerization catalyst;

and provided that:

-   -   one or both of said first olefin and said second olefin is        ethylene;    -   one of said first polymerization catalysts and said second        polymerization catalyst produces an oligomer of the formula        R⁶⁰CH═CH₂ from said ethylene, wherein R⁶⁰ is n-alkyl; and    -   a branched polyolefin is a product of said polymerization        process.

This invention also concerns a polymerization catalyst component,comprising:

(a) a first active polymerization catalyst for said olefins which is aFe or Co complex of a ligand of the formula:

wherein:

-   -   R¹, R² and R³ are each independently hydrogen, hydrocarbyl,        substituted hydrocarbyl, or an inert functional group;    -   R⁴ and R⁵ are each independently hydrogen, hydrocarbyl, an inert        functional group or substituted hydrocarbyl; and    -   R⁶ and R⁷ are aryl or substituted aryl;

(b) a second active polymerization catalyst for said olefins whichcontains one or more transition metals;

(c) a catalyst support; and

(d) optionally one or more polymerization catalyst activators for one orboth of (a) and (b).

Also described herein is a polyolefin containing at least 2 ethylbranches, at least 2 hexyl or longer branches and at least one butylbranch per 1000 methylene groups, and provided that said polyolefin hasfewer than 5 methyl branches per 1000 methylene groups.

This invention also includes a polyolefin, containing about 20 to about150 branches of the formula —(CH₂CH₂)_(n)H wherein n is an integer of 1to 100, provided that said polyolefin has less than about 20 methylbranches per 1000 methylene groups.

DETAILS OF THE INVENTION

In the polymerization processes and catalyst compositions describedherein certain groups may be present. By hydrocarbyl is meant aunivalent radical containing only carbon and hydrogen. By substitutedhydrocarbyl herein is meant a hydrocarbyl group which contains one ormore (types of) substitutents that does not interfere with the operationof the polymerization catalyst system. Suitable substituents in somepolymerizations may include some or all of halo, ester, keto (oxo),amino, imino, carboxyl, phosphite, phosphonite, phosphine, phosphinite,thioether, amide, nitrile, and ether. Preferred substituents are halo,ester, amino, imino, carboxyl, phosphite, phosphonite, phosphine,phosphinite, thioether, and amide. Which substitutents are useful inwhich polymerizations may in some cases be determined by reference toU.S. patent application Ser. No. 08/991,372, filed Dec. 16, 1997, andSer. No. 09/006,031, filed Jan. 12, 1998 (and their corresponding WorldPatent Applications), both of which are hereby included by reference. Byan aryl moiety is meant a univalent group whose free valence is to acarbon atom of an aromatic ring. The aryl moiety may contain one or morearomatic ring and may be substituted by inert groups. By phenyl is meantthe C₆H₅— radical, and a phenyl moiety or substituted phenyl is aradical in which one or more of the hydrogen atoms is replaced by asubstituent group (which may include hydrocarbyl). Preferredsubstituents for substituted phenyl include those listed above forsubstituted hydrocarbyl, plus hydrocarbyl. If not otherwise stated,hydrocarbyl, substituted hydrocarbyl and all other groups containingcarbon atoms, such as alkyl, preferably contain 1 to 20 carbon atoms.

By a polymerization catalyst activator is meant a compound that reactswith a transition metal compound to form an active polymerizationcatalyst. A preferred polymerization catalyst activator is analkylaluminum compound, that is a compound which has one or more alkylgroups bound to an aluminum atom.

By a polymerization catalyst component is meant a composition that byitself, or after reaction with one or more other compounds (optionallyin the presence of the olefins to be polymerized), catalyzes thepolymerization of olefins.

Noncoordinating ions are mentioned and useful herein. Such anions arewell known to the artisan, see for instance W. Beck., et al., Chem.Rev., vol. 88, p. 1405-1421 (1988), and S. H. Strauss, Chem. Rev., vol.93, p. 927-942 (1993), both of which are hereby included by reference.Relative coordinating abilities of such noncoordinating anions aredescribed in these references, Beck at p. 1411, and Strauss at p. 932,Table III. Useful noncoordinating anions include SbF₆ ⁻, BAF, PF₆ ⁻, orBF₄ ⁻, wherein BAF is tetrakis[3,5-bis(trifluoromethyl)phenyl]borate.

A neutral Lewis acid or a cationic Lewis or Bronsted acid whosecounterion is a weakly coordinating anion is also present as part of thecatalyst system. By a “neutral Lewis acid” is meant a compound which isa Lewis acid capable of abstracting X from (II) to form a weaklycoordination anion.

In (II), M is Co or Fe, each X is independently and anion and each X issuch that the total negative charges on X equal the oxidation state ofM. The neutral Lewis acid is originally uncharged (i.e., not ionic).Suitable neutral Lewis acids include SbF₅, Ar₃B (wherein Ar is aryl),and BF₃. By a cationic Lewis acid is meant a cation with a positivecharge such as Ag⁺, H⁺, and Na⁺.

In those instances in which (II) does not contain an alkyl or hydridegroup already bonded to the metal (i.e., X is not alkyl or hydride), theneutral Lewis acid or a cationic Lewis or Bronsted acid also alkylatesor adds a hydride to the metal, i.e., causes an alkyl group or hydrideto become bonded to the metal atom, or a separate compound is added toadd the alkyl or hydride group.

A preferred neutral Lewis acid, which can alkylate the metal, is aselected alkyl aluminum compound, such as R⁹ ₃Al, R⁹ ₂AlCl, R⁹AlCl₂, and“R⁹AlO” (alkylaluminoxanes), wherein R⁹ is alkyl containing 1 to 25carbon atoms, preferably 1 to 4 carbon atoms. Suitable alkyl aluminumcompounds include methylaluminoxane (which is an oligomer with thegeneral formula [MeAlO]_(n)), (C₂H₅)₂AlCl, C₂H₅AlCl₂, and[(CH₃)₂CHCH₂]₃Al. Metal hydrides such as NaBH₄ may be used to bondhydride groups to the metal M.

For (I) and (II) preferred formulas and compounds are found in U.S.patent application Ser. No. 08/991,372, filed Dec. 16, 1997, and Ser.No. 09/006,031, filed Jan. 12, 1998, and preferred groupings andcompounds in these applications are also preferred herein. However thecompound numbers and group (i.e., R^(x)) numbers in these applicationsmay vary from those herein, but they are readily convertible. Theseapplications also describe synthesis of (I) and (II).

There are many different ways of preparing active polymerizationcatalysts from (I) or (II) many of which are described in U.S. patentapplication Ser. No. 08/991,372, filed Dec. 16, 1997, and Ser. No.09/006,031, filed Jan. 12, 1998, and those so described are applicableherein. “Pure” compounds which themselves may be active polymerizationcatalysts may be used, or the active polymerization catalyst may beprepared in situ by a variety of methods.

For instance, olefins may be polymerized by contacting, at a temperatureof about −100° C. to about +200° C. a first compound W, which is aneutral Lewis acid capable of abstracting X⁻ to form WX⁻, provided thatthe anion formed is a weakly coordinating anion; or a cationic Lewis orBronsted acid whose counterion is a weakly coordinating anion.

Which first active polymerization catalysts will polymerize whicholefins, and under what conditions, will also be found in U.S. patentapplication Ser. No. 08/991,372, filed Dec. 16, 1997, and Ser. No.09/006,031, filed Jan. 12, 1998. Monomers useful herein for the firstactive polymerization catalyst include ethylene and propylene. Apreferred monomer for this catalyst is ethylene.

In one preferred process described herein the first and second olefinsare identical, and preferred olefins in such a process are the same asdescribed immediately above. The first and/or second olefins may also bea single olefin or a mixture of olefins to make a copolymer. Again it ispreferred that they be identical, particularly in a process in whichpolymerization by the first and second polymerization catalysts makepolymer simultaneously.

In some processes herein the first active polymerization catalyst maypolymerize a monomer that may not be polymerized by said second activepolymerization catalyst, and/or vice versa. In that instance twochemically distinct polymers may be produced. In another scenario twomonomers would be present, with one polymerization catalyst producing acopolymer, and the other polymerization catalyst producing ahomopolymer, or two copolymers may be produced which vary in the molarproportion or repeat units from the various monomers. Other analogouscombinations will be evident to the artisan.

In another variation of the process described herein one of thepolymerization catalysts makes an oligomer of an olefin, preferablyethylene, which oligomer has the formula R⁶⁰CH═CH₂, wherein R⁶⁰ isn-alkyl, preferably with an even number of carbon atoms. The otherpolymerization catalyst in the process (co)polymerizes this olefin,either by itself or preferably with at least one other olefin,preferably ethylene, to form a branched polyolefin. Preparation of theoligomer (which is sometimes called an α-olefin) by a first activepolymerization-type of catalyst can be found in U.S. patent applicationSer. No. 09/005,965, filed Jan. 12, 1998 (“equivalent” of World PatentApplication 99/02472), and B. L. Small, et. al., J. Am. Chem. Soc., vol.120, p. 7143-7144 (1998), all of which are hereby included by reference.These references describe the use of a limited class of compounds suchas (II) to prepare compounds of the formula R⁶⁰CH═CH₂ from ethylene, andso would qualify as a catalyst that produces this olefin. In a preferredversion of this process one of these first-type polymerization is usedto form the α-olefin, and the second active polymerization catalyst is acatalyst which is capable of copolymerizing ethylene and olefins of theformula R⁶⁰CH═CH₂, such as a Ziegler-Natta-type or metallocene-typecatalyst. Other types of such catalysts include transition metalcomplexes of amidimidates and certain iron or cobalt complexes of (I).The amount of branching due to incorporation of the olefin R⁶⁰CH═CH₂ inthe polymer can be controlled by the ratio of α-olefin formingpolymerization catalyst to higher polymer forming olefin polymerizationcatalyst. The higher the proportion of α-olefin forming polymerizationcatalyst the higher the amount of branching. The homopolyethylenes thatare made may range from polymers with little branching to polymers whichcontain many branches, that is from highly crystalline to amorphoushomopolyethylenes. In one preferred form, especially when a crystallinepolyethylene is being made, the process is carried out in the gas phase.It is believed that in many cases in gas phase polymerization when bothcatalysts are present in the same particle on which polymerization istaking place (for example originally a supported catalyst), the α-olefinis especially efficiently used (polymerized into the resulting polymer).When amorphous or only slightly crystalline homopolyethylenes are beingmade the process may be carried out in liquid slurry or solution.

In the variation of the process described in the immediately precedingparagraph a novel homopolyethylene is produced. By “homopolyethylene” inthis instance is meant a polymer produced in a polymerization in whichethylene is the only polymerizable olefin added to the polymerizationprocess in a single step, reactor, or by simultaneous reactions. Howeverit is understood that the polymer produced is not made by the directpolymerization of ethylene alone, but by the copolymerization ofethylene and α-olefins which are produced in situ. The polymer producedusually contains only branches of the formula (excluding end groups)—(CH₂CH₂)_(n)H wherein n is 1 or more, preferably 1 to 100, morepreferably 1 to 30, of these branches per 1000 methylene atoms. Normallythere will be branches with a range of “n” in the polymer. The amount ofthese branches (as measured by total methyl groups) in the polymerpreferably ranges from about 2 to about 200, especially preferably about5 to about 175, more preferably about 10 to about 150, and especiallypreferably about 20 to about 150 branches per 1000 methylene groups inthe polymer (for the method of measurement and calculation, see WorldPatent Application 96/23010). Another preferable range for thesebranches is about 50 to about 200 methyl groups per 1000 methylenecarbon atoms. It is also preferable (either alone or in combination withthe other preferable features above) that in these branched polymersthere is at least 2 branches each of ethyl and n-hexyl or longer and atleast one n-butyl per 1000 methylene groups, more preferably at least 4branches each of ethyl and n-hexyl or longer and at least 2 n-butylbranches per 1000 methylene groups, and especially preferably at least10 branches each of ethyl and n-hexyl or longer and at least 5 n-butylbranches per 1000 methylene groups. It is also preferred that there aremore ethyl branches than butyl branches in this homopolyethylene. Inanother preferred polymer (alone or in combination with any of the abovepreferred features) there is less than 20 methyl branches, morepreferably less than 2 methyl branch, and especially preferably lessthan 2 methyl branches (all after correction for end groups) per 1000methylene groups.

In the polymerizations to make the “homopolyethylene” only a single highmolecular weight polymer is produced, that is a polymer which has anaverage degree of polymerization of at least 50, more preferably atleast 200, and especially preferably at least 400. The synthesis of thebranched homopolyethylene is believed to be successful in part becausethe catalyst which produces the α-olefin often does so at a ratecomparable with the polymerization rate, both of them, for the sake oflow cost, being relatively rapid.

Likewise, conditions for such polymerizations, particularly forcatalysts of the first active polymerization type, will also be found inall of these patent applications. Briefly, the temperature at which thepolymerization is carried out is about −100° C. to about +200° C.,preferably about −20° C. to about +80° C. The polymerization pressurewhich is used with a gaseous olefin is not critical, atmosphericpressure to about 275 MPa, or more, being a suitable range. With aliquid monomer the monomer may be used neat or diluted with anotherliquid (solvent) for the monomer. The ratio of W:(I), when W is present,is preferably about 1 or more, more preferably about 10 or more whenonly W (no other Lewis acid catalyst) is present. These polymerizationsmay be batch, semi-batch or continuous processes, and may be carried outin liquid medium or the gas phase (assuming the monomers have therequisite volatility). These details will also be found in U.S. patentapplication Ser. No. 08/991,372, filed Dec. 16, 1997, and Ser. No.09/006,031, filed Jan. 12, 1998, and Ser. No. 09/005,965, filed Jan. 12,1998.

In these polymerization processes preferred groups for R⁶ is

-   -   and for R⁷ is

wherein:

-   -   R⁸ and R¹³ are each independently hydrocarbyl, substituted        hydrocarbyl or an inert functional group;    -   R⁹, R¹⁰, R¹¹, R¹⁴, R¹⁵ and R¹⁶ are each independently hydrogen,        hydrocarbyl, substituted hydrocarbyl or an inert functional        group;    -   R¹² and R¹⁷ are each independently hydrogen, hydrocarbyl,        substituted hydrocarbyl or an inert functional group;

and provided that any two of R⁸, R⁹, R¹⁰, R¹¹, R¹², R¹³, R¹⁴, R¹⁵, R¹⁶and R¹⁷ that are vicinal to one another, taken together may form a ring.

Two chemically different active polymerization catalysts are used in thepolymerization described herein. The first active polymerizationcatalyst is described in detail above. The second active polymerizationcatalyst may also meet the limitations of the first activepolymerization catalyst, but must be chemically distinct. For instance,it may have a different transition metal present, and/or utilize aligand which differs in structure between the first and second activepolymerization catalysts. In one preferred process, the ligand type andthe metal are the same, but the ligands differ in their substituents.

Included within the definition of two active polymerization catalystsare systems in which a single polymerization catalyst is added togetherwith another ligand, preferably the same type of ligand, which candisplace the original ligand coordinated to the metal of the originalactive polymerization catalyst, to produce in situ two differentpolymerization catalysts.

However other types of catalysts may also be used for the second activepolymerization catalyst. For instance so-called Ziegler-Natta and/ormetallocene-type catalysts may also be used. These types of catalystsare well known in the polyolefin field, see for instance Angew. Chem.,Int. Ed. Engl., vol. 34, p. 1143-1170 (1995), European PatentApplication 416,815 and U.S. Pat. No. 5,198,401 for information aboutmetallocene-type catalysts, and J. Boor Jr., Ziegler-Natta Catalysts andPolymerizations, Academic Press, New York, 1979 for information aboutZiegler-Natta-type catalysts, all of which are hereby included byreference. Suitable late metal transition catalysts will be found inWorld Patent Applications 96/23010 and 97/02298, both of which arehereby included by reference. Many of the useful polymerizationconditions for these types of catalyst and the first activepolymerization catalysts coincide, so conditions for the polymerizationswith first and second active polymerization catalysts are easilyaccessible. Oftentimes the “co-catalyst” or “activator” is needed formetallocene of Ziegler-Natta-type polymerizations, much as W issometimes needed for polymerizations using the first activepolymerization catalysts. In many instances the same compound, such asan alkylaluminum compound, may be used for these purposes for both typesof polymerization catalysts.

Suitable catalysts for the second polymerization catalyst also includemetallocene-type catalysts, as described in U.S. Pat. No. 5,324,800 andEuropean Patent Application 129,368; particularly advantageous arebridged bis-indenyl metallocenes, for instance as described in U.S. Pat.No. 5,145,819 and European Patent Application 485,823. Another class ofsuitable catalysts comprises the well-known constrained geometrycatalysts, as described in European Patent Applications 416,815,420,436, 671,404, and 643,066 and World Patent Application 91/04257.Also the class of transition metal complexes described in WO 96/13529can be used. Also useful are transition metal complexes ofbis(carboximidamidatonates), as described in U.S. patent applicationSer. No. 08/096,668, filed Sep. 1, 1998.

All the catalysts herein may be “heterogenized” (to form apolymerization catalyst component, for instance) by coating or otherwiseattaching them to solid supports, such as silica or alumina. Where anactive catalyst species is formed by reaction with a compound such as analkylaluminum compound, a support on which the alkylaluminum compound isfirst coated or otherwise attached is contacted with the transitionmetal compounds (or their precursors) to form a catalyst system in whichthe active polymerization catalysts are “attached” to the solid support.These supported catalysts may be used in polymerizations in organicliquids. They may also be used in so-called gas phase polymerizations inwhich the olefin(s) being polymerized are added to the polymerization asgases and no liquid supporting phase is present. The transition metalcompounds may also be coated onto a support such as a polyolefin(polyethylene, polypropylene, etc.) support, optionally along with otherneeded catalyst components such as one or more alkylaluminum compounds.

The molar ratio of the first active polymerization catalyst to thesecond active polymerization catalyst used will depend on the ratio ofpolymer from each catalyst desired, and the relative rate ofpolymerization of each catalyst under the process conditions. Forinstance, if one wanted to prepare a “toughened” thermoplasticpolyethylene that contained 80% crystalline polyethylene and 20% rubberypolyethylene, and the rates of polymerization of the two catalysts wereequal, then one would use a 4:1 molar ratio of the catalyst that gavecrystalline polyethylene to the catalyst that gave rubbery polyethylene.More than two active polymerization catalysts may also be used if thedesired product is to contain more than two different types of polymer.

The polymers made by the first active polymerization catalyst and thesecond active polymerization catalyst may be made in sequence, i.e., apolymerization with one (either first or second) of the catalystsfollowed by a polymerization with the other catalyst, as by using twopolymerization vessels in series. However it is preferred to carry outthe polymerization using the first and second active polymerizationcatalysts in the same vessel(s), i.e., simultaneously. This is possiblebecause in most instances the first and second active polymerizationcatalysts are compatible with each other, and they produce theirdistinctive polymers in the other catalyst's presence.

The polymers produced by this process may vary in molecular weightand/or molecular weight distribution and/or melting point and/or levelof crystallinity, and/or glass transition temperature or other factors.For copolymers the polymers may differ in ratios of comonomers if thedifferent polymerization catalysts polymerize the monomers present atdifferent relative rates. The polymers produced are useful as moldingand extrusion resins and in films as for packaging. They may haveadvantages such as improved melt processing, toughness and improved lowtemperature properties.

In the Examples, all pressures are gauge pressures.

In the Examples the transition metal catalysts were either bought, or ifa vendor is not listed, were made. Synthesis of nickel containingcatalysts will be found in World Patent Application 96/23010, whilesynthesis of cobalt and iron containing catalysts will be found in U.S.patent application Ser. No. 08/991,372, filed Dec. 16, 1997 and Ser. No.09/006,031, filed Jan. 12, 1998.

In the Examples PMAO-IP is a form of methylaluminoxane which stays insolution in toluene, and is commercially available. W440 is aZiegler-Natta type catalyst of unknown structure available from AkzoChemicals, Inc., 1 Livingston Ave., Dobbs Ferry, N.Y. 10522, U.S.A.

EXAMPLES 1-9 AND COMPARATIVE EXAMPLES A-E Ethylene PolymerizationGeneral Procedure

The catalyst was weighed into a reaction vessel and was dissolved inabout 20 mL of distilled toluene. The reaction was sealed andtransferred from the drybox to the hood. The reaction was purged withnitrogen, then ethylene. The PMAO-IP (methylaluminoxane solution) wasthen quickly added to the vessel and the reaction was put under 35 kPaethylene. The reaction ran at room temperature in a water bath to helpdissipate heat from any exotherm. The ethylene was then turned off andthe reaction was quenched with about 15 mL of methanol/HCl solution(90/10 volume %). If polymer was present, the reaction was filtered andthe polymer was rinsed with methanol, then acetone and dried overnightin the hood. The resulting polymer was collected and weighed.

Below for each polymerization the catalysts used are listed

EXAMPLE 1

catalyst 1: 4 mg (0.006 mmol)

catalyst 2: Zirconocene dichloride, from Strem Chemicals, catalog#93-4002, 2 mg (0.006 mmol)

co-catalyst: PMAO-IP; 2.0 mmole Al; 1.0 mL of 2.0M in toluene

duration: 4 h

polymer: 5.322 g yield

EXAMPLE 2

catalyst 1: 4 mg (0.006 mmol)

catalyst 2: 4 mg (0.006 mmol)

cocatalyst: PMAO-IP; 2.0 mmol Al; 1.0 mL of 2.0M in toluene

duration: 4 h

polymer: 2.282 g yield

EXAMPLE 3

catalyst 1: 3.5 mg (0.006 mmol)

catalyst 2: Zirconocene dichloride, from Strem Chemicals, catalog#93-4002, 2 mg (0.006 mmol)

cocatalyst: PMAO-IP; 2.0 mmol Al; 1.0 mL of 2.0M in toluene

duration: 4 h

polymer: 3.651 g yield

EXAMPLE 4

catalyst 1: 3.5 mg (0.006 mmole)

catalyst 2: 4 mg (0.006 mmol)

cocatalyst: PMAO-IP; 2.0 mmol Al; 1.0 mL of 2.0M in toluene

duration: 4 h

polymer: 2.890 g yield

EXAMPLE 5

catalyst 1: 3.5 mg (0.006 mmol)

catalyst 2: 4 mg (0.006 mmol)

cocatalyst: PMAO-IP; 2.0 mmole Al; 1.0 mL of 2.0M in toluene

duration: 4 h

polymer: 3.926 g yield

EXAMPLE 6

catalyst 1: 4 mg (0.006 mmol)

catalyst 2: W440, from Akzo Nobel, 2.3 wt % Ti, 12 mg (0.006 mmole ofTi, based on wt %)

cocatalyst: PMAO-IP; 2.0 mmole Al; 1.0 mL of 2.0M in toluene

duration: 4 h

polymer: 2.643 g yield

EXAMPLE 7

catalyst 1: 3.5 mg (0.006 mmol)

catalyst 2: W440, from Akzo Nobel, 2.3 wt % Ti, 12 mg (0.006 mmole ofTi, based on wt %)

cocatalyst: PMAO-IP; 2.0 mmol Al; 1.0 mL of 2.0M in toluene

duration: 4 h

polymer: 2.943 g yield

EXAMPLE 8

catalyst 1: 4 mg (0.006 mmol)

catalyst 2: 4 mg (0.006 mmol)

catalyst 3: Zirconocene dichloride, from Strem Chemicals, catalog#93-4002, 2 mg (0.006 mmol)

cocatalyst: PMAO-IP; 3.0 mmol Al; 1.5 mL of 2.0M in toluene

duration: 4 h

polymer: 6.178 g yield

EXAMPLE 9

catalyst 1: 3.5 mg (0.006 mmol)

catalyst 2: 4 mg (0.006 mmol)

catalyst 3: Zirconocene dichloride, from Strem Chemicals, catalog#93-4002, 2 mg (0.006 mmol)

cocatalyst: PMAO-IP; 3.0 mmol Al; 1.5 mL of 2.0M in toluene

duration: 4 h

polymer: 4.408 g yield

COMPARATIVE EXAMPLE A

catalyst: Zirconocene dichloride, from Strem Chemicals, catalog#93-4002, 2 mg (0.006 mmol)

cocatalyst: PMAO-IP; 1.0 mmol Al; 0.5 mL of 2.0M in toluene

duration: 4 h

polymer: 2.936 g yield

COMPARATIVE EXAMPLE B

catalyst: 4 mg (0.006 mmol)

cocatalyst: PMAO-IP; 1.0 mmol Al; 0.5 mL of 2.0M in toluene

duration: 4 h

polymer: 1.053 g yield

COMPARATIVE EXAMPLE C

catalyst: 4 mg (0.006 mmol)

cocatalyst: PMAO-IP; 1.0 mmol Al; 0.5 mL of 2.0M in toluene

duration: 4 h

polymer: 2.614 g yield

COMPARATIVE EXAMPLE D

catalyst: 3.5 mg (0.006 mmol)

cocatalyst: PMAO-IP; 1.0 mmol Al; 0.5 mL of 2.0M in toluene

duration: 4 h

polymer: 2.231 g yield

COMPARATIVE EXAMPLE E

catalyst: W440, from Akzo Nobel, 2.3 wt % Ti, 12 mg (0.006 mmole of Ti,based on wt %)

cocatalyst: PMAO-IP; 1.0 mmol Al; 0.5 mL of 2.0M in toluene

duration: 4 h

polymer: 0.326 g yield

EXAMPLES 10-12 Propylene Polymerization General Procedure

The catalyst was weighed into a reaction vessel and was dissolved inabout 20 mL of distilled toluene. The reaction was sealed andtransferred from the drybox to the hood. The reaction was purged withnitrogen, then propylene. The MAO was then quickly added to the vesseland the reaction was put under 35 kPa propylene. Reaction ran at 0° C.in an ice bath. The propylene was then turned off and the reaction wasquenched with about 15 mL of methanol/HCl solution (90/10 volume %). Ifpolymer was present, the reaction was filtered and the polymer wasrinsed with methanol, then acetone and dried overnight in the hood. Theresulting polymer was collected and weighed.

EXAMPLE 10

catalyst 1: 3 mg (0.006 mmol)

catalyst 2: Zirconocene dichloride, from Strem Chemicals, catalog#93-4002, 2 mg (0.006 mmol)

cocatalyst: PMAO-IP; 2.0 mmol Al; 1.0 mL of 2.0M in toluene

duration: 5 h

polymer: 0.471 g yield

EXAMPLE 11

catalyst 1: 3 mg (0.006 mmol)

catalyst 2: 4 mg (0.006 mmol)

cocatalyst: PMAO-IP; 2.0 mmole Al; 1.0 mL of 2.0M in toluene

duration: 5 h

polymer: 1.191 g yield

EXAMPLE 12

catalyst 1: 3 mg (0.006 mmol)

catalyst 2: W440, from Akzo Nobel, 2.3 wt % Ti, 12 mg (0.006 mmole ofTi, based on wt %)

cocatalyst: PMAO-IP; 2.0 mmol Al; 1.0 mL of 2.0M in toluene

duration: 5 h

polymer: 0.238 g yield

EXAMPLES 13-77 AND COMPARATIVE EXAMPLES F-N

In these Examples, compounds A-V and 2 were used as the transition metalcompounds.

For preparation of: compound A see B. L. Small, et al., J. Am. Chem.Soc., vol. 120, p. 7143-7144(1998); compound B see Ewen, et al., J. Am.Chem. Soc., vol. 110, p. 6255-6256(1988); compound C see European PatentApplication 416,815; compound D World patent Application 98/27124;compound E World patent Application 96/23010; compounds G, H, I and Rwere purchased from Boulder Scientific company; compounds K, P and 2were bought from Strem Chemicals Inc.; compound Q was obtained fromAldrich Chemical Co.; compounds S, T, U and V were made by proceduresdescribed in U.S. patent application Ser. No. 08/096,668, filed Sep. 1,1998; compound F was made by reacting ZrCl₄ and the amide lithium salt(see J. Chem. Soc., Dalton Trans. 1994, 657) in ether overnight, andremoving the ether and pentane extraction gave F 69% yield; compound Jwas prepared by modifying the procedure of Journal of OrganometallicChemistry 1993, 459, 117-123; compounds L and M were prepared byfollowing the preparation in Macromolecules, 1995, 28, 5399-5404, andJournal of Organometallic Chemistry 1994, 472, 113-118; compound N wasmade by the procedure described in U.S. Pat. No. 5,096,867; and compoundO was prepared by following a literature procedure (Ferdinand R. W. P.Wild, et al., Journal of Organometallic Chemistry 1985, 288, 63-67).

EXAMPLES 13-17 AND COMPARATIVE EXAMPLES F-G

A 600 mL Parr® reactor was heated up under vacuum and then allowed tocool under nitrogen. In a drybox, to a Hoke® cylinder was added 5 mLtoluene and a certain amount of PMAO-IP (13.5 wt % toluene solution) asshown in Table 1. To a 20 mL vial was added the ethylene(co)polymerization catalyst and 2 mL toluene. The solution was thenpipette transferred to a 300 mL RB flask, followed by addition of 150 mL2,2,4-trimethyl pentane. If catalyst A was used, its toluene suspensionwas syringe transferred to the flask. The flask was capped with a rubbersepta. Both the Hoke® cylinder and the flask were brought out of thedrybox. Under nitrogen protection, the transition metal compoundsolution was cannulated to the reactor. The reactor was pressurized withnitrogen and then the nitrogen was released. The reactor was heated to70° C., then, pressurized 2× to 690 kPa ethylene, venting each time andfinally pressurized to 970 kPa with stirring. The MAO solution was addedfrom the Hoke® cylinder at slightly higher pressure. The ethylenepressure of the reactor was then adjusted to the desired pressure (Table1). The reaction mixture was allowed to stir for certain period of time(Table 1). The heating source was removed. Ethylene was vented to about210 kPa. The reactor was back filled with 1.4 MPa nitrogen and was thenvented to 210 kPa. This was repeated once. The reaction mixture was thencooled to RT (room temperature). The reaction mixture was then slowlypoured into 400 mL methanol, followed by addition of 6 mL conc. HCl.Upon stirring at RT for 25 min, polymer was filtered, washed withmethanol six times and dried in vacuo.

EXAMPLES 18-76 (EXCEPT EXAMPLES 22 AND 23) AND COMPARATIVE EXAMPLES H-N

General procedure for making silica supported catalysts: In a drybox,one of transition metal compounds (but not A), and compound A (0.1 wt %in biphenyl) and silica supported MAO (18 wt % in Al, Albermarle) weremixed with 15 mL of toluene in a 20 mL vial. The vial was shaken for 45minutes at RT. The solid was filtered, washed with 3×5 mL toluene anddried in vacuo for 1 hour. It was then stored in a freezer in the dryboxand was used the same day.

General procedure for gas phase ethylene polymerization by the supportedcatalysts using a Harper Block Reactor: In a drybox, supported catalysts(5.0 mg or 2.0 mg each, except Example 20 where 15.0 mg was used) wereweighed in GC vials. They were placed in a Harper Block Reactor. Thereactor was brought out of the drybox and was charged with 1.21 MPa ofethylene. It was then placed in a 90° C. oil bath for 1 h under 1.12 MPaof ethylene. The reactor temperature reached 85° C. after 23 minutes and87° C. after 35 min. The temperature stayed at 87° C. for the rest ofthe reaction. (Time, temperature and pressure for Examples in Tables7-9, as noted.) Ethylene was vented. Polymers were weighed and thensubmitted for ¹H NMR analysis (TCE-d₂, 120° C.) without purification.Details of these polymerizations are given in Table 2-9.

In Table 10, the branching distribution [in branches per 1,000 methylene(CH₂) groups] of the product polymers of selected examples are given.They were determined by ¹³C NMR (TCB, 120° C.). Methods for measuringthe branching distribution are found in World patent Application96/23010.

In all the Tables, where provided, branching levels in the polymers,Me/1000CH₂ groups, methyl groups per 1000 methylene groups in thepolymer, are measured by the method described in World PatentApplication 96/23010. In the Tables PE is polyethylene, TON is moles ofethylene polymerized/mole of polymerization catalysts (total oftransition metal compounds present)/h, Mn is number average molecularweight, PDI is Mw/Mn where Mw is weight average molecular weight, and Pis ethylene pressure. The PMAO-IP used was 13.5 wt. % in toluene. Theamount of residual α-olefin in the polymer was estimated by ¹H NMR, bymeasurement of the vinylic proton signals of the α-olefin.

TABLE 1 Catalyst, amount Catalyst A Ex. (×10⁻⁶ (×10⁻⁶ P_(C2H4) Time MMAOPE yield #Me Per m.p. Density (IR) No. mole) mole) MPa T (° C.) (min.)(mL) (g) 1000CH₂ (° C.) Mn/PDI (g/cm³) F B, 8.1 0 1.21  70-100 35 4.215.0 1 134 43,700/2.2 0.952 13 B, 8.1 0.26 1.31 81-96 25 4.2 24.0 17116, 103 32,400/2.2 0.914 G C, 2.2 0 1.1 90 30 1.2 11.0 4 132 11,700/19.7 0.940 14 C, 9.5 0.06 1.31 109-126 30 4.8 31.2 8 133125,000/2.7  0.937 15 C, 9.5 0.13 1.34  80-120 36 4.8 30.0 11 11968,400/2.5 0.922 16 C, 4.6 0.26 1.3 71-96 25 2.4 10.3 45 121, 5694,000/2.3 0.895    261/2.8* 17 C, 3.0 2.3 1.41 100-116 43 1.5 16.6 52117, 98 65,000/2.1 0.922  84    214/3.4* *Bimodal distribution due toα-olefins

TABLE 2 Catalyst and PE Ex. amount Catalyst A Al:M:Fe ratio yield Tm No.(×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g) #Me/1000CH₂ (° C.) Mn/PDITON H B, 0.033 0 1000:1:0 0.195 5 127 24,039/5.2 210,000 I C, 0.033 01000:1:0 0.075 4 126 125,451/2.1  82,000 18 B, 0.033 0.001 1000:1:0.030.485 15 120 48,213/4.1 500,000 19 B, 0.033 0.0033 1000:1:0.1 0.159 62125  1,916/24.0 150,000 20 C, 0.099 0.0030 1000:1:0.03 0.200 35 11363,534/2.7 70,000 21 D, 0.033 0.0017 1000:1:0.05 0.228 4 133  2,150/26.2240,000

TABLE 3 Catalyst and PE Ex. amount Catalyst A Al:M:Fe ratio yield No.(×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g) #Me/1000CH₂ TON J H,0.033 0 1000:1:0 0.421 2 460,000 K I, 0.033 0 1000:1:0 0.135 4 150,000 LG, 0.033 0 1000:1:0 0.420 2 460,000 M K, 0.033 0 1000:1:0 0.091 3 99,000N R, 0.033 0 1000:1:0 0.203 2 220,000

TABLE 4 Catalyst and PE α-olefins Ex. amount Catalyst A Al:M:Fe ratioyield #Me/ Tm left in No. (×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g)1000CH₂ (° C.) Mn/PDI TON polymer 24 F, 0.033 0.0017 1000:1:0.05 0.07366 120    213/18.5 76,000 significant 25 G, 0.033 0.0017 1000:1:0.050.503 13 122, 115 41,525/4.7 520,000 almost none 26 H, 0.033 0.00171000:1:0.05 0.752 9 120, 115 54,825/4.7 780,000 almost none 27 I, 0.0330.0017 1000:1:0.05 0.562 31 119 72,982/3.2 580,000 almost none 28 J,0.033 0.0017 1000:1:0.05 0.032 54 —   895/5.6 33,000 small amount 29 K,0.033 0.0017 1000:1:0.05 0.240 16 123  1,124/16.5 250,000 small amount30 L, 0.033 0.0017 1000:1:0.05 0.112 75 116, 102 — 116,000 significant31 M, 0.033 0.0017 1000:1:0.05 0.092 61 119 — 96,000 significant 32 N,0.033 0.0017 1000:1:0.05 0.068 75 124    485/18.3 71,000 small amount 33O, 0.033 0.0017 1000:1:0.05 0.024 15 — — 25,000 almost none 34 P, 0.0330.0017 1000:1:0.05 0.019 12 — — 20,000 small amount 35 Q, 0.033 0.00171000:1:0.05 0.082 40 — — 85,000 significant 36 2, 0.033 0.00171000:1:0.05 0.157 7 — — 160,000 — 37 R, 0.033 0.0017 1000:1:0.05 0.41610 122 37,993/7.3 450,000 almost none 38 S, 0.033 0.0017 1000:1:0.050.056 59 — — 58,000 significant 39 T, 0.033 0.0017 1000:1:0.05 0.023 73— — 24,000 significant 40 U, 0.033 0.0017 1000:1:0.05 0.102 69 — —110,000 significant 41 V, 0.033 0.0017 1000:1:0.05 0.059 78 — — 61,000significant

TABLE 5* Catalyst and PE α-olefins Ex. amount Catalyst A Al:M:Fe ratioyield #Me/ left in No. (×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g)1000CH₂ Mn/PDI TON polymer 42 D, 0.033 0.0033 1000:1:0.10 0.481 83,346/48.6   360,000 significant 43 D, 0.033 0.0082 1000:1:0.25 0.534 14402/156.0 350,000 significant 44 D, 0.033 0.016 1000:1:0.50 0.566 20800/103.0 310,000 significant *Reaction time here is 80 minutes

TABLE 6 Catalyst and PE Ex. amount Catalyst A Al:M:Fe ratio yield #Me/Tm Density No. (×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g) 1000CH₂ (°C.) Mn/PDI TON (g/cm³) 45 H, 0.033 0.0017 1000:1:0.05 0.772 6 12443,791/6.0 800,000 0.930 46 H, 0.013 0.0007 1000:1:0.05 0.367 8 12482,151/3.7 950,000 — 47 I, 0.033 0.0017 1000:1:0.05 0.566 38 11470,462/4.0 590,000 0.909 48 I, 0.013 0.0007 1000:1:0.05 0.226 32 — —590,000 — 49 B, 0.033 0.0010 1000:1:0.03 0.442 8 127 52,673/4.9 460,0000.928 50 B, 0.033 0.0010 1000:1:0.03 0.563 17 120 52,350/4.9 600,000 —51 B, 0.013 0.0004 1000:1:0.03 0.134 16 — — 350,000 — 52 H, 0.033 0.00101000:1:0.03 0.699 — — — 740,000 — 53 N, 0.013 0.0004 1000:1:0.03 0.362 6124 55,102/5.0 960,000 — 54 I, 0.033 0.0010 1000:1:0.03 0.376 15 11898,599/4.0 400,000 — 55 G, 0.033 0.0010 1000:1:0.03 0.665 5 12438,693/6.0 700,000 —

TABLE 7* Catalyst and PE Ex. amount Catalyst A Al:M:Fe ratio yield #Me/Tm No. (×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g) 1000CH₂ (° C.)Mn/PDI TON 56 B, 0.033 0.0017 1000:1:0.05 0.740 22 118, 101 54,573/4.0380,000 57 B, 0.013 0.0007 1000:1:0.05 0.206 24 — — 270,000 58 H, 0.0330.0017 1000:1:0.05 1.158 7 121 92,063/4.9 600,000 59 H, 0.013 0.00071000:1:0.05 0.651 12 — — 850,000 60 I, 0.033 0.0017 1000:1:0.05 0.439 24102 102,798/3.8  230,000 61 I, 0.013 0.0007 1000:1:0.05 0.390 25 — —510,000 62 G, 0.033 0.0017 1000:1:0.05 0.871 9 121 45,311/4.7 450,000*Two h at 70° C. and 2.4 MPa ethylene pressure.

TABLE 8* Catalyst and PE Ex. amount Catalyst A Al:M:Fe ratio yield No.(×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g) TON 63 B, 0.013 0.00071000:1:0.05 0.143 370,000 64 B, 0.013 0.0007 1000:1:0.05 0.115 300,00065 H, 0.013 0.0007 1000:1:0.05 0.305 790,000 66 H, 0.013 0.00071000:1:0.05 0.215 560,000 67 I, 0.013 0.0007 1000:1:0.05 0.093 240,00068 I, 0.013 0.0007 1000:1:0.05 0.108 280,000 69 G, 0.013 0.00071000:1:0.05 0.349 900,000 One h at 90° C. at 2.4 MPa ethylene pressure.

TABLE 9* Catalyst and PE Ex. amount Catalyst A Al:M:Fe ratio yield #Me/No. (×10⁻⁶ mole) (×10⁻⁶ mole) M = Zr, Ti or Fe (g) 1000CH₂ Mn/PDI TON 70B, 0.033 0.0017 1000:1:0.05 0.534 37 42,448/3.4 280,000 71 B, 0.0330.0017 1000:1:0.05 0.489 45 — 250,000 72 H, 0.033 0.0017 1000:1:0.050.969 17 77,142/4.8 500,000 73 H, 0.033 0.0017 1000:1:0.05 1.027 11 —530,000 74 I, 0.033 0.0017 1000:1:0.05 0.442 34 96,383/4.2 230,000 75 I,0.033 0.0017 1000:1:0.05 0.466 32 — 240,000 76 G, 0.033 0.00171000:1:0.05 0.710 8 39,693/4.9 370,000 *Two h at 60° C., 2.4 MPaethylene pressure

TABLE 10 Ex. No. Total Me Me Et Pr Bu Am Hex and higher 15 10.5 0 4.6 02.4 0 4.3 13 16 0 6.5 0 3.2 0 6.5 26 6.9 0 2.9 0 0.4 0 2.5 47 23 0 8.6 04.7 0 10.7 49 8.1 0 3.6 0 1.3 0 3.1

EXAMPLE 22

In a drybox, 1.7 mg Compound E and 1.0 mg Compound A were mixed with 40mL toluene in a Schlenk flask. This was brought out of the drybox andwas purged with ethylene for 15 min at 0° C. MAO toluene solution (0.64mL 13.5 wt %) was injected. The mixture was allowed to stir under 0 kPaethylene at 0° C. for 12 min. Methanol (100 mL) was injected, followedby 1 mL conc. HCl. Upon stirring for 25 min at RT, the white solid wasfiltered, washed with 6×20 mL methanol and dried in vacuo. White solid(2.9 g) was obtained. ¹HNMR in TCE-d₂ at 120° C.: 44Me/1000CH₂. Thepolymer contained a significant amount of α-olefins.

EXAMPLE 23

In a drybox, 30.5 mg of Compound A was mixed with 30.5 g biphenyl in a100 mL Pyrex® glass bottle. This was stirred in a 100° C. bath for 25minutes, during which time Compound A dissolved in biphenyl to form adeep green solution. The solution was allowed to cool down to becomesolid. A 0.1 wt % Compound A/biphenyl homogeneous mixture was obtained.

EXAMPLE 77

A 600 mL Parr® reactor was heated up under vacuum and then allowed tocool under nitrogen. In a drybox, to a 300 mL RB flask was added 150 mL2,2,4-trimethylpentane. The flask was capped with a rubber septum. Theflask was brought out of the drybox. Under nitrogen protection, the2,2,4-trimethylpentane solvent was cannulated into the reactor. Thereactor was pressured up with nitrogen and then nitrogen was released.This was repeated one more time. The reactor was heated to 70° C. Thenin a drybox, 160 mg supported catalyst(made by following the generalprocedure of preparing silica supported catalysts, it contained 0.0011mmole of compound B, 0.000057 mmole compound A and 1.1 mmole of MAO) wasmixed with 4 mL cyclohexane and was transferred to a 5 mL gas tightsyringe with long needle. This was brought out of the drybox and wasinjected into the reactor under nitrogen protection (positive nitrogenpressure). The reactor was pressured up with 1.2 MPa of nitrogen, thenreleased to 14 kPa. This was repeated one more time. Under stirring, thereactor was pressured up with ethylene to 1.2 MPa. The reaction mixturewas allowed to stir at between 70° C. to 97° C. for 60 min. Heatingsource was removed. Ethylene was vented to about 210 kPa. The reactorwas back filled with 1.4 MPa nitrogen and was released to 140 kPa. Thiswas repeated twice. The solution was poured into 300 mL methanol. Thepolymer was filtered, washed with 6×50 mL methanol and dried in vacuo.White polymer (19.7 g) was obtained. ¹HNMR in TCE-d₂ at 120° C.:34Me/1000CH₂. Mw=98,991; Mn=35,416(PDI=2.8). Density: 0.902 g/cm³. MeltIndex: 1.03(190° C.). ¹³CNMR(120° C., TCE-d₂): Total Me was 29.4(Me=0;Et=10.8; Pr=0.0; Bu=6.0; Hex and higher=11.7).

1. A process for the polymerization of olefins, comprising, contactingunder polymerizing conditions: (a) a first active polymerizationcatalyst for said olefins which is a Fe or Co complex of a ligand of theformula:

wherein: R¹, R² and R³ are each independently hydrogen, hydrocarbyl,substituted hydrocarbyl, or an inert functional group; R⁴ and R⁵ areeach independently hydrogen, hydrocarbyl, an inert functional group orsubstituted hydrocarbyl; and R⁶ and R⁷ are aryl or substituted aryl; (b)a second active polymerization catalyst for said olefins which containsone or more transition metals; (c) at least one first olefin capable ofbeing polymerized by said first active polymerization catalyst; and (d)at least one second olefin capable of being polymerized by said secondactive polymerization catalyst.
 2. The process as recited in claim 1wherein said second active polymerization catalyst is a Ziegler-Natta ora metallocene type polymerization catalyst.
 3. The process as recited inclaim 1 wherein said first olefin and said second olefin are bothethylene.
 4. The process as recited in claim 1 wherein said first olefinis ethylene.
 5. The process as recited in claim 1 wherein said firstolefin and said second olefin is each independently one or both ofethylene or propylene.
 6. The process as recited in claim 1 wherein saidpolymerization with said first active polymerization catalyst and saidpolymerization with said second polymerization catalyst are carried outsimultaneously.
 7. The process as recited in claim 1 wherein said firstolefin and said second olefin are the same.
 8. (canceled)
 9. (canceled)10. (canceled)
 11. (canceled)
 12. (canceled)
 13. (canceled) 14.(canceled)
 15. (canceled)
 16. (canceled)
 17. (canceled)
 18. (canceled)19. (canceled)
 20. (canceled)
 21. (canceled)
 22. (canceled) 23.(canceled)
 24. (canceled)
 25. (canceled)
 26. The process as recited inclaim 2 wherein said first olefin is ethylene.
 27. The process asrecited in claim 2 wherein said first olefin and said second olefin iseach independently one or both of ethylene or propylene.
 28. Apolymerization catalyst component, comprising: (a) a first activepolymerization catalyst for ethylene which is a Fe or Co complex of aligand of the formula:

wherein: R¹, R² and R³ are each independently hydrogen, hydrocarbyl,substituted hydrocarbyl, or an inert functional group; R⁴ and R⁵ areeach independently hydrogen, hydrocarbyl, an inert functional group orsubstituted hydrocarbyl; and R⁶ and R⁷ are aryl or substituted aryl; and(b) a second active polymerization catalyst for one or more olefinswhich contains one or more transition metals.
 29. The polymerizationcatalyst component as recited in claim 28 which also comprises acatalyst support.
 30. The polymerization catalyst component as recitedin claim 29 which also comprises a catalyst activator.
 31. Thepolymerization catalyst component as recited in claim 28 wherein saidsecond active polymerization catalyst is a Ziegler-Natta or ametallocene polymerization catalyst.
 32. The polymerization catalystcomponent as recited in claim 30 wherein said second activepolymerization catalyst is a Ziegler-Natta or a metallocenepolymerization catalyst.
 33. The polymerization catalyst component asrecited in claim 32 wherein said catalyst activator is an alkylaluminumcompound.
 34. The polymerization catalyst component as recited in claim28 wherein said support is alumina, silica or a polyolefin.